【Composition】

Uncatalyzed fluorosilicone rubber based on fluorosilicone gun,and mixed evenly with some kinds of fillers and additives

【Characteristics】

MY-R-M2000 is pale-yellow translucent fluorosilicone base, it's suitable for extrusion application. It has

integrated advantages that both the silicone rubber and fluororubber have.

1. Wide application temperature range(-60℃~200℃);

2. Similar resistance to  solvent  &fuel oil  to  that of fluororubber;

3. Keeping high tensile force retention at high temperature which is like silicone rubber,

4. High insulation;

5.High selective permeability meets requirements of environmental protection.

Therefore it can be used as seal material in special condition with requirement of resistance to high and/or low temperature,oil and some other chemical mediums.

Properties obtained using 1.5phr DCBP.Molded 15min at 110℃,post-cured 4hr at 200℃.If other cure temperature needed,vulcanization system shall be changed.

【Application】

1.Suitable for extrusion application.

2.Can be applied in aviation industry,auto industry, petroleum chemical industry,medical and health care industry and military industry

【Package】

Plastic bags.12.5kg per sack,2 sacks in 1 carton.

【Storage】

Shall be stored in dry and ventilated places at room temperature (25℃).Validity is 1 year.

【Transportation】

Transpoit it as non-dangerous cargo.

【Attention】

1.The product shall be kept neutral,avoid being contacted with acid,alkaline substance.

2.The product can flow under its own weight.Keep it in good condition of packing during transportation and application in order it not to flow out.